| Title | Managing the Double-Edged Sword of Ni3+in Sputter-Deposited NiOx by Interfacial Redox Reactions for Efficient Perovskite Solar Cells |
| Authors | Peng, Zongyang Zuo, Zhuang Qi, Qi Hou, Shaocong Fu, Yongping Zou, Dechun |
| Affiliation | Peking Univ, Coll Chem & Mol Engn, Ctr Soft Matter Sci & Engn, Beijing Natl Lab Mol Sci,Key Lab Polymer Chem & Ph, Beijing 100871, Peoples R China Wuhan Univ, Sch Elect Engn & Automat, Wuhan 430072, Peoples R China |
| Keywords | NICKEL-OXIDE LAYER PASSIVATION PERFORMANCE ROLES |
| Issue Date | Jan-2023 |
| Publisher | ACS APPLIED ENERGY MATERIALS |
| Abstract | Nickel oxide (NiOx) is widely used as a promising hole transport material for perovskite solar cells (PSCs). A high concentration of Ni3+ in the NiOx film is generally beneficial for charge transport of the PSCs; however, chemical redox reactions between surface Ni3+ and perovskite materials result in decomposition of perovskite materials, which causes carrier recombination and impedes charge transport at the perovskite-NiOx interface. Herein, we employ magnetron sputtering to fabricate NiOx thin films with adjustable Ni3+ concentrations to optimize the hole-transporting properties. A thin layer of phenylethylamine iodide (PEAI) is further introduced to reduce the detrimental Ni3+ at the surface of NiOx, which eliminates the formation of undesirable defects and chemical species when in contact with the perovskite layer, leading to a dramatic increase in the power conversion efficiency (PCE) from 16.37 to 20.01%, which is one of the best performance using sputtered charge transport layers. The unencapsulated devices retain 88% of their initial PCE after storage in a nitrogen atmosphere for 1000 h under light. We further perform solar cell capacitance simulator (SCAPS) simulation to understand the effects of bulk and interfacial charge transport on the performance of PSCs, which agree with our experimental results. This work not only highlights the double-edged sword effect of the Ni3+ content on the performance and stability of PSCs but also demonstrates a simple yet effective strategy to avoid the undesirable reaction between Ni3+ and perovskite materials in the fabrication of PSCs with sputter-deposited NiOx. |
| URI | http://hdl.handle.net/20.500.11897/670986 |
| ISSN | 2574-0962 |
| DOI | 10.1021/acsaem.2c03260 |
| Indexed | SCI(E) |
| Appears in Collections: | 化学与分子工程学院 高分子化学与物理教育部重点实验室 |